Free Sample AFS30-35 casting Chromite Sand/chrome ore sand

Free Sample AFS30-35 casting Chromite Sand/chrome ore sand

Product Description

 foundry chromite sand for foundry:

Foundry chromite sand is a natural process products of chromite through the broken screen classification, chrome ore, its main chemical composition of cr2o3, this kind of sand heated volume stability, high thermal conductivity, when in contact information with the molten metal, not only has good resistance to basic slag, not with ferric oxide and other chemical reactions, and itself has the characteristics of the solid phase sintering, can be a very good prevent the infiltration of molten metal, avoid to touch sand defects, suitable for all kinds of stainless steel, alloy steel and carbon steel gradually shape the original sand core and coating.

chromite sand.png

 

Physical and chemical Of Chromite sand:

 Contact us by click here.

 

Physics

Index

Chemistry

Index

Bulk Density

2.5-3g/cm³

Cr2O3

≥46.0% 

PH Value

7-9

SiO2

≤1.0%

Cr/Fe

1.55:1

Fe2O3

≤26.5%

   Filling Density

2.6 g/cm³

CaO

≤0.30%

Percent Moisture

≤0.1

MgO

≤10%

The sintered

1600°C

AI2O3

≤15.5%

Sintering Temperature

2180°C

P

≤0.003%

     Melting Point

>1800°C

C

≤0.003%

Regular size

                             AFS 25-35 AFS25-30 AFS30-35 AFS35-40                                             AFS40-45 AFS45-50 AFS50-55 AFS55-60 AFS60-65

Packaging & Shipping

 Packing.jpg

Customer visit

 2.jpg

Production

 The production process of foundry chromite sand for foundry:

Step1: chrome ore raw material is processed by water washing.

Step2, drying raw materials to remove water;

Step3, drying raw materials into the vibrating screen, screening out the size of the customer needs;

Step4, the size of the sieve for magnetic separation, the purpose of iron and silicon removal. After magnetic separation, the chromium content reached more than 46% and the silicon content was less than 1%.

Step5: package the finished product.